Materiales ceramicos con propiedades de baja expansion termica y/o alta conduccion ionica

  1. CARRASCO RODRIGUEZ M. PILAR
Supervised by:
  1. Carmen Guillem Director

Defence university: Universitat de València

Year of defence: 1992

Committee:
  1. Agustín Escardino Benlloch Chair
  2. Santiago García Granda Secretary
  3. Juan Rodríguez-Carvajal Committee member
  4. Pedro Durán Botia Committee member
  5. Eduardo Martínez Tamayo Committee member
Department:
  1. INORGANIC CHEM

Type: Thesis

Teseo: 34840 DIALNET

Abstract

EL ESTUDIO DE LA RELACION COMPOSICION-ESTRUCTURA-PROPIEDADES EN LA FAMILIA DE COMPUESTOS NZP PERMITE CONTROLAR LAS PROPIEDADES DE ESTAS CERAMICAS MEDIANTE LA COMPOSICION. LAS DISOLUCIONES SOLIDAS NASN2-XZRX(PO4)3, NATI2-XSNX(PO4)3 Y NAGE2-XTIX(PO4)3 SE HAN PREPARADO POR EL METODO CERAMICO REALIZANDOSE EL ESTUDIO DE COMO AFECTA LA COMPOSICION A LA ESTRUCTURA Y A LAS PROPIEDADES DE EXPANSION TERMICA Y CONDUCTIVIDAD IONICA. LAS CERAMICAS MONOFASICAS OBTENIDAS PRESENTAN DISCONTINUIDADES EN SUS PROPIEDADES DEBIDAS A LAS TRANSICIONES DE FASE QUE EXPERIMENTAN. LA CONDUCTIVIDAD IONICA DEL COMPUESTO LIZR2(PO4)3 Y SUS DERIVADOS, PREPARADOS POR EL METODO GEL, ES ELEVADA PRESENTANDO ESTOS COMPUESTOS EL INCONVENIENTE DE SU BAJA DENSIFICACION Y QUE AL PRESENTAR UNA ESTRUCTURA ABIERTA ES POSIBLE LA INTRODUCCION DE LAS DISTINTAS ESPECIES PRESENTES EN EL MEDIO DE SINTESIS. ESTO HACE DIFICIL LA IDENTIFICACION DE LAS ESPECIES CONDUCTORAS.