Materiales ceramicos basados en fases cristalinas aluminosilicatosmullita

  1. SALES SEGARRA, MANUELA
Supervised by:
  1. Javier Alarcón Navarro Director

Defence university: Universitat de València

Year of defence: 1997

Committee:
  1. José Moratal Mascarell Chair
  2. María Ángeles Villegas Broncano Secretary
  3. José María Amigó Descarrega Committee member
  4. Francisco Bosch Reig Committee member
  5. Luis María Esquivias Fedriani Committee member
Department:
  1. INORGANIC CHEM

Type: Thesis

Teseo: 61022 DIALNET

Abstract

ESTA TESIS DOCTORAL SE ENCUADRA DENTRO DE UN PROYECTO DE INVESTIGACION SOBRE PIGMENTOS CERAMICOS EN EL PROGRAMA NACIONAL DE MATERIALES. UN PIGMENTO CERAMICO ES UNA SUSTANCIA INORGANICA CUYA ESTRUCTURA CRISTALINA SEA ESTABLE A ALTA TEMPERATURA Y PRESENTA RESISTENCIA AL CHOQUE TERMICO. LA MULLITA ES UN COMPUESTO QUE CUMPLE ESTOS REQUERIMIENTOS. EL OBJETIVO DE ESTA TESIS ES EL ESTUDIO DE MATERIALES COMPUESTOS DE MULLITA Y UNA FASE CROMOFORA ESPINELA NIAL2O4 O COAL2O4 PARA SU USO COMO SISTEMAS PIGMENTANTES. EN ESTE ESTUDIO SE HAN APLICADO TECNICAS DE SINTESIS SOL-GEL PARA OBTENER LOS MATERIALES A BAJA TEMPERATURA Y CON EL DESARROLLO MICROESTRUCTURAL MAS ADECUADO A SU APLICACION. EN LA CARACTERIZACION DE ESTOS MATERIALES SE HAN APLICADO LAS TECNICAS HABITUALES: DIFRACCION DE RAYOS-X, ANALISIS TERMICO, ESPECTROSCOPIA IR, ESPECTROSCOPIA ULTRAVIOLETA-VISIBLE Y MICROSCOPIA ELECTRONICA. DE ESTA FORMA HA SIDO POSIBLE SEGUIR LA REACTIVIDAD DE LOS SISTEMAS Y LAS MICROESTRUCTURAS POR INTRODUCCION DE TI4+ Y NI2+ EN LA MULLITA.